| Typical composition in % |
|
| C |
≤ 0,025 |
| Si |
0,90 |
| Mn |
1,80 |
| P |
≤ 0,025 |
| S |
≤ 0,015 |
| Cr |
18,50 |
| Ni |
12,00 |
| Mo |
≤ 2,60 |
| Co |
≤ 0,20 |
| Cu |
≤ 0,20 |
| N |
0,06 |
| Classification |
|
| EN 12072 G/W/P/S |
19 12 3 L Si |
| DIN 8556 |
1.4430 |
| AWS ER |
316LSi |
| Base materials |
| Joining of stainless Cr-Ni-Mo and Cr-Ni steels, stabilised or non-stabilised, e.g. 316, 316L and 316Ti as well as 304, 304L, 321 and 347, for service temperatures up to 400oC. Also for stainless Cr steels with max 19 % Cr. |
| Resistance against corrosion |
| Good resistance to general and, owing to low C content, intergranular corrosion. The Mo content gives good resistance also to pitting. |
| Physical properties (Approx. values) at 20° C |
|
| Yield strength Rp0,2 [MPa] |
400 (20°C); 290 (400°C) |
| Tensile strength Rm [MPa] |
610 (20°C); 440 (400°C) |
| Elongation A [%] |
37 (20°C); 29 (400°C) |
| Reduction of area [%] |
68 |
| Notched impact strengthV [J] |
130 (20°C); 50 (-196°C) |
| Hardness [Vickers] |
160 |
| Ferrite number from standard analysis DeLong |
11 |
| Heat conductivity at temperature ° Celsius |
20; 100; 300; 500 |
| Heat conductivity [W/m °C] |
15; 16; 19; 21 |
| Thermal expansion per °C, from 20°C - 400°C |
18 x 10-6 |
| Density [g/cm³] |
7,9 |
| Shielding gas |
| MIG: Ar+1-3% O2, Ar+1-3% CO2, Ar+He+O2, Ar+He+CO2, Ar+He+CO2+H2 |
| WIG: Ar, He, Ar+He, Ar+2-5% H2 |
| Dimensions |
|
| MIG-wires [mm] |
0,8; 1,0; 1,2; 1,6 |
| TIG-rods [mm] |
1,0; 1,2; 1,6; 2,0; 2,4; 3,2; 4,0 |
Images of the packs may be found here...
| Spools |
| BS 300 / 15 kg |
| Drum / 300 kg |
TIG-rods are packed in boxes of 5 kg. The length is 1.000 mm.